Cellular molded article in mold pattern having surface skin and producing method thereof

ABSTRACT

A cellular molded article in a mold pattern having the surface skin, which has an excellent releasing property from a metal mold as well as an excellent printing property of a design formed on a surface of metal mold, and a producing method thereof are provided.  
     The cellular molded article in a mold pattern having the surface skin and a producing method thereof, in which, at least a face of surface skin material, which contacts with a metal mold, is an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as its matrix, and pre-expanded beads, which are employed for an expansion molding in a mold pattern, are pre-expanded beads of an olefin line resin.

TECHNICAL FIELD

[0001] This invention relates to a cellular molded article in a mold pattern having a surface skin, which is used for such as the interior trim material of an automobile, and a producing method thereof.

BACKGROUND OF THE INVENTION

[0002] As a conventional producing method of a cellular molded article having a surface skin in this kind, it is known as a so-called simultaneous unification molding to one piece that, for example, on either one of two metal molds by which a mold pattern is formed, a surface skin material of thermoplastic resin is arranged, and after clamping the metal molds, pre-expanded beads are fed into this mold pattern, then the pre-expanded beads are expanded and melt united each other by steam heating, and at the same time, these pre-expanded beads and the above mentioned surface skin material of thermoplastic resin are melt united together to one piece.

[0003] In this simultaneous unification molding to one piece, in each inside of the above mentioned two metal molds, a chamber connected with a steam valve, a decompression valve and such others are provided. And, on the one metal mold to which the above mentioned surface skin material will be arranged, a plural number of decompression holes which connect with the above mentioned chamber are provided, at the same time, on the other metal mold, a plural number of decompression holes which connect with the above mentioned chamber are provided. And, at a time of the above mentioned expansion molding, by means of supplying steam into the mold pattern from the steam holes on the above mentioned other metal mold, the filled pre-expanded beads in this mold pattern are heat expanded.

[0004] In this step, in order to make an effective expansion molding by pre-heating the above mentioned surface skin material, before arranging this surface skin material, by means of supplying steam into the above mentioned chamber, the above mentioned other metal mold is often pre-heated.

[0005] However, in a case of preheating the above mentioned one metal mold as in the above, if an olefin line thermoplastic resin elastmer is employed as the above mentioned surface skin material, after molding it, at a time of mold releasing of the cellular molded article in the mold pattern having the surface skin from the above mentioned one metal mold, the above mentioned surface skin material will stick on the above mentioned one metal mold, and therefore it will often cause a hard release from the above mentioned one metal mold.

[0006] Usually, before releasing it, it is cooled down by water or the like, but it will not be sufficient. While, a long time cooling is not preferable due to a longer producing cycle.

[0007] At a time of releasing the cellular molded article in the mold pattern having the surface skin after the end of molding, if the above mentioned surface skin material sticks on the metal mold as in the above, an automatic releasing of the molded article from the molding machine becomes hard, subsequently, it will raise its production cost by a longer time of molding cycle, or by addition of equipment, tools or the like for releasing the molded article from the molding machine. Furthermore, as releasing the stuck molded article by force from the face of metal mold, there is a problem that design of the surface skin will be deteriorated.

SUMMARY OF THE INVENTION

[0008] This invention is to solve the above mentioned problems, and even in a case of preheating the above mentioned one metal mold, sticking the surface skin material on the above mentioned one metal mold will practically not be appeared, and therefore, it is an object to provide a producing method of the cellular molded article in the mold pattern having the surface skin and a molded article thereby, which are free from problems of the molding operation.

DISCLOSURE OF THE INVENTION

[0009] To achieve the above mentioned object, an essential feature residing in the invention which is claimed is that, a measure for producing method of the cellular molded article in the mold pattern having a surface skin is that, a producing method which is, after thermoforming of a surface skin material along by a metal mold face of either one of two metal molds which compose a mold pattern, by means of expansion molding in this mold pattern, the above mentioned surface skin material is melt united to one piece with a surface of cellular molded article in the mold pattern to be molded, and at least a face of the above mentioned surface skin material, which contacts with a metal mold, is an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as its matrix, and pre-expanded beads, which are employed for an expansion molding in the mold pattern, are pre-expanded beads of an olefin line resin.

[0010] An essential feature residing the invention which is claimed is that, a measure that at least a face of the above mentioned surface skin material contacting with a metal mold is composed of a domain, which contains a polyethylene line resin as its composing raw material resin and is formed by dynamic curing, and an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as a matrix, and pre-expanded beads to be employed for an expansion molding in the mold pattern are pre-expanded beads of an olefin line resin.

[0011] An essential feature residing in the invention which is claimed is that, a measure is that the above mentioned olefin line pre-expanded beads are pre-expanded beads of a propylene line resin.

[0012] An essential feature residing in the invention which is claimed is that, a measure is that the above mentioned olefin line pre-expanded beads are pre-expanded beads of a polyethylene line resin.

[0013] An essential feature residing in the invention which is claimed is that, a measure is that the above mentioned olefin line resin as a matrix is a polypropylene line resin.

[0014] An essential feature residing in the invention which is claimed is that, a measure is that the above mentioned polyethylene line resin which is not included as a matrix is a linear low density polyethylene line resin.

[0015] An essential feature residing in the invention which is claimed is that, a measure is that at least the one metal mold is composed of an aluminum line metal.

[0016] An essential feature residing in the invention which is claimed is that on the surface of the above mentioned one metal mold, a design pattern, which will be printed on a sheet at a time of thermal forming of the sheet, is attached.

[0017] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the surface skin which is prepared by that, after thermo-forming of a surface skin material along by either one of metal mold face of two metal molds which compose a mold pattern, by means of expansion molding in this mold pattern, the above mentioned surface skin material is melt united to one piece with a surface of cellular molded article to be molded, and at least one face of the above mentioned surface skin material which contacts with a metal mold is composed of an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as a matrix, and pre-expanded beads which will be employed for an expansion molding in the mold pattern are pre-expanded beads of an olefin line resin.

[0018] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the surface skin is that, at least one face of the above mentioned surface skin material which contacts with a metal mold is an olefin line thermoplastic elastomer sheet composed of an olefin line resin without containing a polyethylene line resin, and pre-expanded beads, which will be employed for an expansion molding in the mold pattern, are pre-expanded beads of an olefin line resin.

[0019] An essential feature residing in the invention which is claimed is that, a measure for the interior trim material of an automobile comprises the cellular molded article in the mold pattern having the surface skin which is claimed.

[0020] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the surface skin is that pre-expanded beads of the above mentioned olefin line resin are pre-expanded beads of a polypropylene line resin.

[0021] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the Surface skin is that pre-expanded beads of the above mentioned olefin line resin are pre-expanded beads of a polyethylene line resin.

[0022] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the surface skin is that the above mentioned olefin line resin as a matrix is a polypropylene line resin.

[0023] An essential feature residing in the invention which is claimed is that, a measure for the cellular molded article in the mold pattern having the surface skin is that the above mentioned polyethylene line resin which is not included as a matrix is a linear low density polyethylene line resin.

BRIEF DESCRIPTION OF THE DRAWINGS

[0024] For the better understanding of the invention as well as other objects and features thereof, reference is made to the following detailed description to be read in conjunction with the accompanying drawings, wherein:

[0025]FIG. 1 illustrates a sectional side view of the cellular molded article in the mold pattern having the surface skin of a polyolefin line resin.

[0026]FIG. 2 illustrates a sectional side explanation view that, in a producing method of cellular molded article in the mold pattern having the surface skin of polyolefin line resin, it is shown a state that a TPO surface skin material is arranged on the surface of the one metal mold and then clamped.

[0027]FIG. 3 illustrates a sectional side explanation view in which a state of feeding pre-expanded beads of a polyolefin line resin into a mold pattern is shown.

[0028]FIG. 4 illustrates a sectional side explanation view in which, after feeding pre-expanded beads of a polyolefin line resin, a state of feeding steam into a mold pattern is shown.

[0029]FIG. 5 illustrates a sectional side explanation view in which a state of vacuuming inside of a mold pattern is shown.

[0030]FIG. 6 illustrates a sectional side explanation view in which a state of feeding steam into a mold pattern and expanding pre-expanded beads of a polyolefin line resin are shown.

[0031]FIG. 7 illustrates a sectional side view of the cellular molded article in the mold pattern having the surface skin of a polyolefin line resin, which is released from a mold pattern and thus edge part of the surface skin material is attached as it is molded.

[0032]FIG. 8 illustrates a sectional side view of the cellular molded article in the mold pattern having the surface skin of a polyolefin line resin, in which a dual layer surface skin material is employed.

[0033] In the above mentioned drawings, marks represent as follows;

[0034] 1 cellular molded article in the mold pattern having the surface skin of polyolefin line resin

[0035] 2 cellular molded article of a polyolefin line resin

[0036] 3 TPO surface material

[0037] 4 mold pattern

[0038] 5 the one metal mold

[0039] 6 the other metal mold

[0040] 7 inside of the mold pattern

[0041] 8 pre-expanded beads of a polyolefin line resin

[0042] 13 thermoplastic surface skin material for outer layer

BEST MODE FOR PRACTICING THE INVENTION

[0043] Embodiments of this invention are described below based on the attached drawings. As illustrated in FIG. 1, the cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1 comprises the cellular molded article in the mold pattern of a polyolefin line resin 2, which is formed to such as U-shape in sectional side view, and TPO (olefin line thermoplastic elastomer) surface skin material 3, which is melt united to one piece with surface 2 a of said cellular molded article in the mold pattern of a polyolefin line resin.

[0044] The above mentioned cellular molded article in the mold pattern of polyolefin line resin 2 is a molded article by expansion molding in the mold pattern of pre-expanded beads of a polyolefin line resin pre-expanded beads. As the above mentioned polyolefin line resin, for example, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, ethylene-vinyl acetate copolymer, propylene homopolymer, ethylene-propylene random copolymer, ethylene-propylene-butene random terpolymer, propylene-vinyl chloride copolymer, propylene-butene copolymer, propylene-maleic anhydride copolymer, and polyethylene line resin or polypropylene line resin of poly (butene-1) or the like can be mentioned among others, and these can be used alone or as a mixture of not less than two of them.

[0045] This polyolefin line resin is preferably not cross linked however, it may also be cross-linked by using a peroxide, radiation or the like.

[0046] Furthermore, a mixture of this polyolefin line resin and other thermoplastic resin can be employed. As such kind of thermoplastic resin, in a case of blending with the above mentioned polypropylene line resin, for example, low density polyethylene, linear low density polyethylene, aromatic vinyl line polymer, polybutene, and ionomer can be mentioned among others. While, in case of blending with the above mentioned polyethylene line resin, for example, aromatic vinyl line polymer, polybutene and ionomer can be mentioned among others. And in these cases, as an amount of the thermoplastic resin to be blended with is preferably not more than 20 parts by weight against 100 parts by weight of a polyolefin line resin, more preferably 5 to 10 parts by weight.

[0047] The above mentioned pre-expanded beads of polyolefin line resin 8 can be produced for example by a process that a polyolefin line resin as in the above is molded to pellet shape in advance, this polyolefin line resin pellet is made to be impregnated with a volatile foaming agent in an autoclave and then is dispersed in water in keeping stirring, and after heating it up until a prescribed foaming temperature, by means that this dispersed pellet in water is released into a low pressure zone, and thus, it is produced in a pre-expanded state.

[0048] As an expansion rate when these pre-expanded beads of a polyolefin line resin 8 are expanded in the mold pattern, in a case of less than 3 times, buffer property or the like of an obtained cellular molded article in the mold pattern of polyolefin line resin 2 tends to be reduced, while in a case of more than 60 times, shrinkage of cellular molded article in the mold pattern of a polyolefin line resin 2 becomes too large and also its strength or the like becomes low due to excessive softness, therefore, it is desirable 3 to 60 times, preferably 5 to 50 times, more preferably 8 to 45 times, and most preferably 10 to 35 times. As such pre-expanded beads of a polyolefin line resin 8, for example, Eperan PP (trade name, made by Kanegafuchi Chemical Industry, Co. expansion rate is 15 times) can be suitably employed among others.

[0049] An olefin line copolymer rubber which is employed as the above mentioned TPO surface skin material (olefin line thermoplastic elastomer) 3 is a non-regular type random elastic copolymer with an olefin as its main component, which is, for example, ethylene-propylene line copolymer rubber, ethylene-propylene-nonconjugated diene line rubber, ethylene-butene-nonconjugated diene line rubber, or propylene-butadiene line copolymer rubber can be mentioned among others. Among these, an ethylene-propylene-nonconjugated diene line rubber is particularly preferable. As a nonconjugated diene, dicyclopentadiene, 1,4-hexadiene, cyclooctadiene, methylene norbornane, ethylidene norbornane can be mentioned among others.

[0050] An olefin line copolymer rubber is usually cross linked, and a suitable elasticity is caused by this. Therefore, if a cross linking by a peroxide or a radiation works effectively, such method will not be limited whatsoever.

[0051] A preferable olefin line resin, which is employed for the above mentioned TPO surface skin material (olefin line thermoplastic elastomer) 3, is a polypropylene line resin, and as a preferable said polypropylene line resin, a polypropylene and/or a random or block copolymer resin of propylene and α-olefin having two or more carbon atoms. As a typical example of α-olefin having two or more carbon atoms, ethylene, 1-butene, 1-pentene, 3-methyl-1-butene, 1-hexene, 1-decene, 3-methyl-1-pentene, 4-methyl-1-pentene or 1-octene can be mentioned among others.

[0052] In the present invention, an olefin line resin as in this description is preferably excluding a polyethylene line resin, and even if a polyethylene polymer is included, the minimum amount of it can improve its releasing property from a mold pattern. The reason of this property is not cleared yet, but it is thought that, because of a low softening temperature of polyethylene line resin, this resin sticks on a metal mold, and thus, its releasing property gets worse. From the above assumption, for example, in a case of 100% by weight of olefin line resin, blending amount of a polyethylene polymer is not more than 15% by weight, preferably not more than 5% by weight, and more preferably not more than 1% by weight. The most preferably, it should be reduced further however, as long as achieving an object of the present invention, it is not limited to these.

[0053] That is, in the present invention, an olefin line resin without containing a polyethylene line resin as a matrix is described as in the above definition. TPO surface skin material 3 comprises the above mentioned olefin line copolymer rubber (domain) and an olefin line resin (matrix), and a ratio of each of them can be determined or selected by one's discretion according to its object. And as a cross linking agent, which makes a partial cross linking of the above mentioned each mixture, in general, an organic peroxide is suitably employed.

[0054] In a producing method of the above mentioned TPO surface skin material, if necessary, an auxiliary agent such as cross linking auxiliary agent, flow promoter, inorganic filler, antioxidant, weather-proof agent, anti-static agent, pigment can be blended therewith.

[0055] Furthermore, as a coating material for scratch protection, which comprises a thermoplastic elastomer and which is coated on the sheet surface, it is preferably an urethane line or acrylic line coating material.

[0056] As a processing method of a laminated surface skin material in which such material is employed, it can be mentioned among others that, during a processing or after the processing of sheet molding by a method of calendar molding or T-die extrusion molding of a thermoplastic elastomer according to the above mentioned method or the like, a resinous cellular article layer is laminated, and then, in its lower stream process, a coating material is coated on a surface of thermoplastic elastomer which will be the utmost outer layer by a coating machine such as gravure coater.

[0057] Next, a producing method of the cellular molded article in the mold pattern having the surface skin of polyolefin line resin 1 will be explained. As illustrated in FIG. 2 to FIG. 7 inclusive, a producing method of the cellular molded article in the mold pattern having the surface skin of olefin line resin 1, which is relating to this embodiment of the present invention, is that on the one metal mold 5 of two metal molds 5 and 6, which compose mold pattern 4, TPO surface skin material 3 is arranged and clamped them, after then pre-expanded beads of a polyolefin line resin 8 are fed into this mold pattern 7, and, by means of steam heating, these pre-expanded beads of a polyolefin line resin 8 are expanded to make melt uniting together, and at the same time, these pre-expanded beads of a polyolefin line resin 8 are melt united to one piece with the above mentioned TPO surface skin material 3.

[0058] That is, as illustrated in FIG. 2, the above mentioned TPO surface skin material 3 is arranged on the above mentioned one metal mold 5, and then the mold pattern is clamped.

[0059] At this stage, the above mentioned mold pattern 4 is, for example, composed of two metal molds 5 and 6, which are capable to clamp and open in vertical direction.

[0060] In these two metal molds 5 and 6, the above mentioned one metal mold 5 is, for example, composed of a concave shape in sectional side view, and chamber 5 b is formed in its inside, and a plural number of decompression holes 5 c, which are connected with the above mentioned chamber 5 b, are formed on its surface 5 a side. And, the above mentioned chamber 5 b is connected with a steam valve A1, a decompression valve B1 and a drain valve C1 respectively. The other metal mold 6 a is, for example, composed of a convex shape in sectional side view, and chamber 6 b is formed in its inside, and a plural number of steam holes 6 c, which are connected with the above mentioned chamber 6 b, are formed on its surface 6 a side. And, the above mentioned chamber 6 b is connected with a steam valve A2, a decompression valve B2 and a drain valve C2 respectively, and feeder 10 for feeding pre-expanded beads of polyolefin line resin 8 into the above mentioned mold pattern 7 is provided.

[0061] Arranging the above mentioned TPO surface skin material 3 on surface 5 a of the one metal mold 5 may be made by that the above mentioned TPO surface skin material 3 is formed in advance to a suitable shape to conform to surface 5 a shape of the above mentioned one metal mold 5 by such as vacuum forming, however, as is in this embodiment, in a case of arranging it by heat forming such as vacuum forming, there is a merit that the labor for forming it in advance can be omitted. And, as a thermo-forming of this TPO surface skin material 3, it is not limited to vacuum forming but other forming such as compression molding can be applied.

[0062] At this stage, as a method for vacuum forming, the above mentioned TPO surface skin material 3 is heat-softened beforehand, and it is contacted with the one metal mold 5 as it is, thereafter decompression valve B1, which is connected with the above mentioned chamber 5 b, is opened or like that.

[0063] In this case, by means that the above mentioned one metal mold 5 is heated up to a prescribed temperature by steam or a heater which is separately mounted on or the like, temperature drop of heat-softened TPO surface skin material 3 to be contacted with said the one metal mold 5 can be minimized, thus there is a merit that a design pattern of the one metal mold 5 can be effectively printed on TPO surface skin material 3. Further, during the heat molding or in the subsequent expansion molding in the mold pattern, in order to prevent a heat drop of TPO surface skin material 3, heating up by such as a heater may continue during the thermo-forming or even in after it, or a stepwise heating which is changing the setting temperature in stepwise from the beginning may also be done.

[0064] And, in a case that the above mentioned TPO surface skin material 3 comprises a polyolefin line resin, when the temperature of the one metal mold 5 before the thermo-forming operation is at in a range of 60 to 150° C., preferably at 60 to 130° C., more preferably at 70 to 120° C., as the above mentioned TPO surface skin material 3 can be thermo-formed in a suitable softening condition, there is a merit to make a good finishing.

[0065] While, in a case that the cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1 to be obtained by this process is, for example, required to have a fitting tool or the like, on surface 6 a of the above mentioned other metal mold 6, a prescribed shaped inserting member (not shown) is arranged in advance, and at a time of expanding operation in the mold pattern of the above mentioned pre-expanded beads of a polyolefin line resin 8, this inserting member may be melt united to one piece with the cellular molded article in the mold pattern of a polyolefin line resin 2.

[0066] Next, as illustrated in FIG. 3, pre-expanded beads of a polyolefin line resin 8 are fed into mold pattern 7 from the above mentioned feeder 10.

[0067] At this stage, as TPO surface skin material 3 is arranged on surface 5 a of the above mentioned one metal mold 5 in a condition of clamped, the inside air can be evacuated by only steam holes 6 c of the above mentioned other metal mold 6, consequently, to make a smooth feeding of the above mentioned pre-expanded beads of a polyolefin line resin 8, a small opening between the two metal molds may be made so that these pre-expanded beads of a polyolefin line resin 8 will not go through, but the inside air can be evacuated from this small opening at a time of the feeding.

[0068] And, the above mentioned pre-expanded beads of a polyolefin line resin 8 may be fed into the above mentioned mold pattern 7 in a state that a compressed gas is penetrated into their insides in advance and an inner pressure in each of them is given, or may be fed in a compressed state by a compressed gas, or may be fed as they are without giving an inside pressure or compressing.

[0069] Thereafter, as illustrated in FIG. 4, a steam valve A2, which connects with chamber 6 b of the above mentioned other metal mold 6, is opened, and steam S is fed into mold pattern 7 through the above mentioned steam holes 6 c, and the above mentioned pre-expanded beads of a polyolefin line resin 8 are heat expanded.

[0070] At this stage, by means that the above mentioned pre-expanded beads of a polyolefin line resin 8 are pre-heated in advance at a lower temperature than the temperature of their melt uniting together, before the regular heating of these pre-expanded beads of a polyolefin line resin 8 at a higher temperature than the temperature of their melt uniting together, pre-expanded beads of a polyolefin line resin 8 can be made to a sufficiently heated up to a state without causing a problem of melt uniting each other.

[0071] Furthermore, after a pre-heating as in the above, by steaming the above mentioned pre-expanded beads of a polyolefin line resin 8 with steam S, as can be effectively utilizing the latent heat of fed steam S in between the above mentioned pre-expanded beads of a polyolefin line resin 8, particularly, in a case of forming a thick cellular molded article in the mold pattern of a polyolefin line resin 2 or the like, there is a merit that the above mentioned pre-expanded beads of a polyolefin line resin 8 can be more uniformly heated.

[0072] And, after the pre-heating, steaming can be made by continuous steam S supply, or by suspending steam S supply, or, if necessary, in a condition of opening drain valve C2.

[0073] After steaming of the above mentioned pre-expanded beads of a polyolefin line resin 8 by steam S, there remains drain (moisture) in between the above mentioned pre-expanded beads of a polyolefin line resin 8, and if a regular heating is made as they are, there will happen insufficient melt uniting of pre-expanded beads of a polyolefin line resin 8 each other. Therefore, evacuation of the above mentioned drain is desirable.

[0074] As a method for evacuation of this drain, for example, as illustrated in FIG. 5, a method that, decompression valve B2, which is connected with chamber 6 b of the above mentioned other metal mold 6, is opened and vacuuming inside of mold pattern 7 through the above mentioned steam holes 6 c, or a method that, making a slit between two metal molds 5 and 6 by making a small opening in the mold pattern 4, then a high temperature and dry air, which is however not so high as melt uniting temperature of pre-expanded beads of polyolefin line resin 8, is penetrated therein so as to evacuate the drain through the above mentioned slit, can be mentioned among others.

[0075] Subsequently, the regular heating is carried out at a higher temperature than the temperature of melt uniting each other of the above mentioned pre-expanded beads of a polyolefin line resin 8. This regular heating is carried out, as illustrated in FIG. 6, by supplying steam S into mold pattern 7 from the above mentioned steam holes 6 by opening the above mentioned steam valve A2. At this step, as described in the above, in a case that, after the steaming by steam S, vacuuming of the above mentioned mold pattern 7 is carried out for evacuation of the drain, the above mentioned steam S for the regular heating can be supplied more smoothly into mold pattern 7.

[0076] In addition, the temperature of steam S at this stage is preferably higher than the temperature at which the above mentioned pre-expanded beads of a polyolefin line resin 8 are melt uniting each other. However, in a case of excessively high temperature, shrinkage of obtained cellular molded article in the mold pattern of a polyolefin line resin 2 will become excessively large.

[0077] After the regular heating as described in the above, in order to transfer the heat by steam S into the above mentioned pre-expanded beads of a polyolefin line resin 8 sufficiently, it is desirable to keep in its condition.

[0078] Subsequently, by opening the above mentioned mold pattern 4, as is illustrated in FIG. 7, cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1 a which is having edge part 3 c can be obtained.

[0079] And, before opening the mold pattern, the above mentioned mold pattern 4 may be cooled down in advance. Also, cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1 a which has been obtained is preferably dried by such as keeping it in a dried room, right after released it from mold pattern 4. While, as is described in this embodiment, in a case that the above mentioned edge part 3 c is formed by an excessive edge part of the above mentioned TPO surface skin material 3, after releasing it from the mold pattern, as is described in the above, after drying it or before keeping it in a drying room, by cutting off the above mentioned edge part 3 c, cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1, which is illustrated in FIG. 1, can be obtained.

[0080] As is described in the above, the above mentioned pre-expanded beads of a polyolefin line resin 8 is pre-heated and steamed by steam S, and then, by making a regular heating, when cellular molded article in the mold pattern of a polyolefin line resin 2 is produced from pre-expanded beads of a polyolefin line resin 8, simultaneously said cellular molded article in the mold pattern of polyolefin line resin 2 can be tightly melt united to one piece with the above mentioned TPO surface skin material 3, and in further, cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 1, in which the above mentioned cellular molded article in the mold pattern of a polyolefin line resin 2 is free from insufficient melt uniting of pre-expanded beads of a polyolefin line resin 8, can be produced.

[0081] Cellular molded article in the mold pattern having the surface skin of a polyolefin line resin 11 illustrated in FIG. 8 is an example that, on surface 3 a of the above mentioned TPO surface skin material 3, thermoplastic surface skin material for outer layer 13 of one layer is laminated.

[0082] When such laminated TPO surface skin material 3 with at least one layer of thermoplastic surface skin material for outer layer 13 is melt uniting to one piece with the above mentioned cellular molded article in the mold pattern of a polyolefin line resin 2, as TPO surface skin material 3 is hidden by the above mentioned thermoplastic surface skin material for outer layer 13, by means of employing thermoplastic surface skin material for outer layer 13 which comprises a material which will not stick with the one metal mold 5, or in further, has a better printing property for the design so that a better appearance can be made, accordingly, there will not need to consider about a sticking problem of TPO surface skin material 3 with the one metal mold 5 nor about its appearance problem, and therefore, there is a merit that this TPO surface skin material 3 can be made from a desirable composition in consideration of a better melt uniting property with pre-expanded beads of a polyolefin line resin, a better vacuum forming property or like that.

[0083] Furthermore, in the above embodiment 1 and 2 which are illustrated in FIG. 7 and FIG. 8, it was described of a case that the above mentioned one metal mold 5 is a concave mold (female mold) of which sectional side view is concave shape, however, it is not limited to this, but it can also be made that the above mentioned one metal mold is a convex mold (male mold) and the other metal mold 6 is a concave mold (female mold).

[0084] As an use of the cellular molded article in the mold pattern having the surface skin by the present invention, various industrial products such as sports goods field or parts for building and housing can be mentioned. As the interior trim material for an automobile, an instrument panel, console box, arm rest, head rest, door trim, rear panel, pillar trim, sun visor, trunk room trim, trunk lid trim, head liner, globe box and ceiling material can be mentioned among others.

EXAMPLE

[0085] Next, more details of the present invention will be described by examples of the invention however, it is not limited to these examples.

Example 1 to 3

[0086] In a female mold and a male mold which compose a mold pattern, after arranging a surface skin material on the above mentioned female mold by vacuum forming, an expansion molding in this mold pattern was carried out. In inside of a portion on which a cavity face of the above mentioned female mold is composed, a flow line for passing a thermo-medium is formed in meandering shape, and by means of passing steam through this flow line, the temperature of cavity face is kept as shown in Table 1. And, on the above mentioned male mold, steam holes for feeding steam into the mold pattern at a time of expansion molding and a feeder for supplying pre-expanded beads were mounted.

[0087] In this stage, a thermoplastic resin sheet of polyolefine line resin (TPO sheet) as the above mentioned surface skin material was employed, and after heating this sheet, it was arranged on the above mentioned female mold, then it was shaped by a vacuum pump. As pre-expanded beads, Eperan PP (trade name, produced by Kanegafuchi Chemical Industry Co., expansion rate was 15 times, its inner pressure was 2 kg/cm²·G given by air pressure in a pressure container in advance) was employed, and after clamping the mold pattern, these pre-expanded beads were fed into the mold pattern through the above mentioned feeder.

[0088] After the feeding of pre-expanded beads, steam (vapor pressure was 1.5 kg/cm²·G) was fed into the mold pattern through the steam holes mounted on the above mentioned male mold, and pre-heated. Then, after steaming of the pre-expanded beads, the drain and steam were suctioned and evacuated by employing a vacuum pump. Thereafter, steam (vapor pressure was 3.2 to 3.7 kg/cm²·G) was fed into the mold pattern again through the above mentioned steam holes and a regular heating was carried out, and then, after cooled down by water, by opening the mold pattern, the cellular molded article in the mold pattern having the surface skin was obtained. While, cooling of the female mold during the above mentioned water cooling time was carried out by feeding a cooled water into the above mentioned flow line.

Comparative Example 1 to 2

[0089] The cellular molded article in the mold pattern having the surface skin was obtained by the same manner as in example 1 to 3 except employing the surface skin material shown in Table 1.

Comparative Example 3 to 6

[0090] The surface temperature of female mold pattern was changed as shown in Table 1, and comparative example 4 shows the result in which Pef PPAM (trade name of Toray company) was employed as the surface skin material.

[0091] In addition, at a time of opening the mold pattern in example 1 to 3 and comparative example 1 to 6, a presence of sticking of the surface skin material with the female mold pattern was observed. Also, a surface appearance of each of the obtained cellular molded article in the mold pattern having the surface skin was examined. Its result is shown in Table 1.

[0092] [Evaluation Standard]

[0093] Presence of sticking of the surface skin material with the female mold pattern;

[0094] ⊚: none of presence of sticking with the metal mold

[0095] ∘: some presence of sticking with the metal mold, but it can be released without trouble

[0096] ▴: presence of sticking with the metal mold is observed and automatic releasing from the metal mold is difficult

[0097] ×: strong sticking with the metal mold and cannot be released from the metal mold

[0098] Printing property of the design to the molded article;

[0099] ⊚: design of the metal mold is sufficiently printed on

[0100] ∘: design of the metal mold is almost printed on

[0101] ▴: design of the metal mold is printed on, but defect is observed

[0102] ×: design of the metal mold is not sufficiently printed on

[0103] Melt uniting property of the beads with the surface skin material

[0104] ⊚: beads are tightly melt united with the surface skin material

[0105] ∘: beads are melt united with the surface skin material

[0106] ▴: beads are melt united with the surface skin material but not tightly

[0107] ×: beads are not sufficiently united with the surface skin material TABLE 1 Sticking of Surface temperature surface skin Melt uniting Composition of surface of female mold (° C.) material to Printing property of skin material Vacuum Expansion female mold property of beads with Domain Matrix forming molding pattern design surface skin Example 1 TPO-a R-PP (a) 95 100  ⊚ ⊚ ⊚ EPDM B-PP Example 2 TPO-b R-PP (a) 90 90 ◯ ◯˜⊚ ⊚ EPDM R-PP Example 3 TPO-c R-PP (a) 95 95 ⊚ ⊚ ⊚ EPDM LLDPE Comparative TPO-a LLDPE 100  95 X ▴˜◯ ⊚ example 1 EPDM B-PP Comparative TPO-a R-PP (a) 95 95 ▴ ▴˜◯ ⊚ example 2 EPDM R-PP Comparative TPO-a R-PP 50 50 ⊚ ▴˜X X example 3 EPDM B-PP Comparative TPO-a R-PP 50 50 ⊚ ▴˜X ⊚ example 4 (*1) EPDM LLDPE B-PP Comparative TPO-a R-PP 50 95 X ▴˜X ⊚ example 5 EPDM LLDPE B-PP Comparative TPO-a R-PP 95 50 ▴˜X ▴˜◯ X example 6 EPDM LLDPE R-PP

[0108] In the above Table 1, it is shown that: TPO-a WT312B, trade name, made by Sumitomo Chemical Industry TPO-b 4652, trade name, made by Sumitomo Chemical Industry TPO-c 8030N, trade name, made by Mitsui Petroleum Chemical Co R-PP(a) S-131, trade name, made by Sumitomo Chemical Industry LLDPE FW201-O, trade name, made by Sumitomo Chemical Industry *1 Pef PPAM 15025, trade name, made by Toray Co.

[0109] Effectiveness of the Invention

[0110] A producing method for the cellular molded article in the mold pattern having the surface skin and a molded article thereby which are relating to the present invention exhibit an excellent effect in printing of a design of metal mold onto a surface skin material, and an excellent automatic releasing property from a mold metal. Accordingly, there are a lot of advantageous effects such as a good appearance, easy recycling or light weight.

[0111] Although the invention has been described in its preferred form with certain degree of particularity, it is understood that the present disclosure of the preferred form has been changed in the details of construction and the combination and arrangement of parts may be resorted to without departing from the spirit and the scope of the invention as hereinafter claimed. 

What is claimed is:
 1. A producing method of a cellular molded article in a mold pattern having a surface skin is that, after thermoforming of a surface skin material along by a metal mold face of either one of two metal molds which compose a mold pattern, by means of expansion molding in this mold pattern, the above mentioned surface skin material is melt united to one piece with a surface of cellular molded article in the mold pattern to be molded, wherein it is characterized in that at least a face of the above mentioned surface skin material, which contacts with a metal mold, is an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as its matrix, and pre-expanded beads, which are employed for an expansion molding in the mold pattern, are pre-expanded beads of an olefine line resin.
 2. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, at least a face of the above mentioned surface skin material contacting with a metal mold is composed of a domain, which contains a polyethylene line resin as its composing raw material resin and is formed by dynamic curing, and an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as a matrix, and pre-expanded beads to be employed for an expansion molding in the mold pattern are pre-expanded beads of an olefin line resin.
 3. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, the above mentioned olefin line pre-expanded beads are pre-expanded beads of a polypropylene line resin.
 4. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, the above mentioned pre-expanded beads of an olefin line resin are pre-expanded beads of a polyethylene line resin.
 5. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, the above mentioned olefin line resin as a matrix is a polypropylene line resin.
 6. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, the above mentioned polyethylene line resin which is not included as a matrix is a linear low density polyethylene line resin.
 7. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, at least the one metal mold is composed of an aluminum line metal.
 8. A producing method of the cellular molded article in the mold pattern having the surface skin as claimed in claim 1, wherein it is characterized in that, on the surface of the above mentioned one metal mold, a design pattern, which will be printed on a sheet at a time of thermal forming of the sheet, is attached.
 9. A cellular molded article in the mold pattern having the surface skin, which is characterized in that, the cellular molded article in the mold pattern having the surface skin which is prepared by that, after thermoforming of a surface skin material along by either one of metal mold face of two metal molds which compose a mold pattern, by means of expansion molding in this mold pattern, the above mentioned surface skin material is melt united to one piece with a surface of cellular molded article to be molded, and at least one face of the above mentioned surface skin material which contacts with a metal mold is composed of an olefin line thermoplastic elastomer sheet which is composed of an olefin line resin without containing a polyethylene line resin as a matrix, and pre-expanded beads which will be employed for an expansion molding in the mold pattern are pre-expanded beads of an olefin line resin.
 10. A cellular molded article in the mold pattern having the surface skin as claimed in claim 9, wherein it is characterized in that, the cellular molded article in the mold pattern having the surface skin is that, at least one face of the above mentioned surface skin material which contacts with a metal mold is an olefin line thermoplastic elastomer sheet composed of an olefin line resin without containing a polyethylene line resin, and pre-expanded beads, which will be employed for an expansion molding, are pre-expanded beads of an olefin line resins.
 11. The interior trim material of an automobile comprises a cellular molded article in the mold pattern having the surface skin as claimed in claim
 9. 12. A cellular molded article in the mold pattern having the surface skin as claimed in claim 9, wherein it is characterized in that, pre-expanded beads of the above mentioned olefin line resin are pre-expanded beads of a polypropylene line resin.
 13. A cellular molded article in the mold pattern having the surface skin as claimed in claim 9, wherein it is characterized in that, pre-expanded beads of the above mentioned olefin line resin are pre-expanded beads of a polyethylene line resin.
 14. A cellular molded article in the mold pattern having the surface skin as claimed in claim 9, wherein it is characterized in that, the above mentioned olefin line resin as a matrix is a polypropylene line resin.
 15. A cellular molded article in the mold pattern having the surface skin as claimed in claim 9, wherein it is characterized in that, the above mentioned polyethylene line resin which is not included as a matrix is a linear low density polyethylene line resin. 